| Place of Origin: | Jiangsu, China |
|---|---|
| Brand Name: | Wuxi East Group |
| Certification: | SGS, VOC |
| Model Number: | EG-701.1 |
| Minimum Order Quantity: | 100 Kilograms |
| Price: | USD+3.2-3.5+KG |
| Packaging Details: | 25 KG/ Carton |
| Delivery Time: | 15 work days |
| Payment Terms: | L/C, T/T |
| Supply Ability: | 300 Ton/Tons per Month |
| CAS No.: | 9009-54-5 | Other Names: | Hot Melt Adhesive |
|---|---|---|---|
| MF: | Mixture | EINECS No.: | 230-391-5 |
| Classification: | Hot Melt Adhesives | Main Raw Material: | Polyolefin |
| Usage: | Packing, Industry | Type: | Polyolefin |
| Product Name: | Polyolefin Hot Melt Adhesives | Material: | Polyolefin |
| Colour: | Milk White | Shape: | Block Or Pillow |
| Size: | 25kg | MOQ: | 100 |
| Packing: | Carton | Characteristic: | High Initial Strength, High Viscosity |
| Port: | Shanghai | ||
| Highlight: | 9009 54 5 Polyolefin Hot Melt Adhesive,Polyolefin Hot Melt Adhesive Milk White,Milk White Polyolefin Glue |
||
High Initial Strength Polyolefin Based Hot Melt Adhesives for Mattress Sofa
Hot melt adhesives for mattresses enable non toxic bonding.
Hot melt adhesives for mattresses are becoming increasingly popular, as they offer a non- toxic, environmentally-friendly solution for mattress bonding.
These adhesives bond components together at the highest possible efficiency and at the lowest application costs.
Polyolefin hot melt adhesives offer a wider application range, higher heat stability, as well as improved adhesion at cold temperatures.
Depending on the formulation, open times can be set from less than one second to almost one minute, or even offer an unlimited open time as a semi-adhesive.
|
Product Name
|
Polyolefin Hot Melt Adhesives for Mattress Manufacture
|
|
Material
|
Block
|
|
Colour
|
Milk White
|
|
Size
|
25kg
|
|
MOQ
|
100
|
|
Storage Temperature
|
5~35ºC
|
|
Storage Time
|
2 Years
|
|
Characteristic
|
High initial strength,
High viscosity
Hydrolysis resistance after composite
|
|
Applied Products
|
Mattress, luggage
|
|
Service Temperature
|
165ºC-185ºC
|
|
Softening point
|
93± 5 ºC
|
|
Melt viscosity
|
1700 ± 500MPa · s (180 ºC)
|